회사 소식 Study Highlights Electrode Calenderings Impact on Lithiumion Battery Performance

Imagine a small lithium-ion battery electrode undergoing precise calendering—what microscopic transformations occur, and how do they influence energy density, power density, and cycle life? Electrode calendering, a critical manufacturing step, tailors battery performance by fine-tuning microstructural properties. This article explores the modeling, scientific principles, and optimization strategies behind this process.

Calendering involves compressing electrode materials between rotating rollers to achieve uniform density and surface finish. Typically performed above the binder’s glass transition temperature, this process minimizes residual stress while homogenizing material distribution. Though mechanically straightforward, it governs complex interactions between particles, binders, and conductive additives.

Researchers often model electrodes as homogeneous materials compressed by rollers under linear load (q _L ), defined as the applied force (F _N ) multiplied by the coating width (ω _C ). The contact area (A _Γ ) between rollers depends on their radius (r _R ), electrode dimensions, and gap width (δ _Γ ). Longer dwell times in the roller gap promote particle rearrangement, reduce shear stress, and enhance compaction uniformity.

Post-compression, elastic recovery occurs as the load diminishes. The compaction ratio (Π) quantifies thickness reduction, where Π = 1 – (δ _E,a /δ _E,initial ). This metric reflects the balance between plastic deformation (irreversible) and elastic rebound.

Calendering primarily alters three electrode properties—thickness, porosity, and tortuosity—each with cascading effects on performance:

Thicker electrodes increase active material loading but extend ion transport paths, raising ohmic resistance. While beneficial for energy density, this trade-off reduces power density and high-rate capability. Thin electrodes, conversely, improve mechanical integrity and cycle life by minimizing delamination risks.

Commercial electrodes typically target ~30% porosity to balance ionic conductivity and electronic contact. Higher porosity improves electrolyte wetting but risks uneven current distribution and accelerated aging. Low porosity enhances rate capability by forming continuous conductive networks, though excessive compaction may impede ion transport.

Binder content significantly influences porosity: higher binder concentrations reduce elastic rebound, yielding denser structures. Temperature also plays a role—elevated temperatures soften binders, improving conductivity through enhanced particle contacts.

Smaller pores and particles lower tortuosity, facilitating ion flow. However, nanoscale active materials, while improving rate performance, may exacerbate side reactions. Cathodes benefit more from calendering than anodes due to their inherently lower conductivity; compaction strengthens particle contacts without compromising elastic energy.

Excessive compression risks pore collapse, hindering ion diffusion and electrolyte wetting. This can degrade rate capability, increase polarization, and compromise safety. Dense structures also impede SEI formation and promote mechanical stress, potentially causing microcracks and binder fatigue over cycles.

Optimizing calendering requires balancing mechanical and electrochemical factors within narrow parameter windows. Advanced modeling techniques and material-specific studies are needed to mitigate stress-induced degradation while maximizing performance. Future research may explore novel process parameters and heterogeneous material responses to refine this pivotal manufacturing step.